I-Polysilicon Ditrctional Soldificatiion Furnace
Isicelo
Esi sixhobo sibandakanyeka kwimveliso ye-ingot yelanga kunye nokucocwa kwezixhobo ze-semiconductor.Isetyenziswa ngokubanzi kwimveliso yesilivere-based based, i-cobalt-based based alloys yobushushu obuphezulu, kunye neemveliso ezikumgangatho ophezulu ezenziwe ngala ma-alloys ziqhele ukwenziwa kwishishini le-injini ye-injini ye-aerospace, isithuthi, i-biomedical field, i-chemistry field kunye nemimandla yokonwabisa.
Iimbonakalo
Ukuchaneka kolawulo oluphezulu, uhlengahlengiso lwasimahla lwesantya se-cystallization, ukuchasana kwegraphite okanye indlela yokufudumeza yokuncibilika kwe-induction, ukunyusa ukunyibilika kokunyibilika, isantya sokunyibilika ngokukhawuleza.Umbane okhethekileyo wokufudumeza wamkelwa ukugcinwa kobushushu obuqinileyo, obunenqanaba lesithathu langoku elilinganayo kunye neendleko zokugcina eziphantsi.Ii-curves ze-148 zokufudumeza zingasetwa kunye nomlawuli weqondo lokushisa rhoqo.Umzimba wesithando somlilo esiphezulu usetyenziswa kwigumbi lomlilo, elineqondo eliphezulu le-vacuum kunye nesantya sokumpompa ngokukhawuleza.
Iiparamitha zobuGcisa
Ukunyibilika Umthamo | 10-450KG |
Amandla | 40-450KW |
Ubushushu obuyiliweyo | 1700℃ |
Ubushushu bokusebenza | 1450℃ |
Iqondo lokunyuka kobushushu | 40℃/min |
Ubushushu bomlilo obufanayo | +5℃ |
Vacuum encinci | 6.67 * 10-2Pa |
Izinga lokunyuka koxinzelelo | 0.01PaL/S |
Uxinzelelo lokunyuka kwamaxabiso | 0.05Mpa |
Indlela yokuphosa ingot | ukuqina kwesikhokelo kunye ne-crucible falling/ukubamba ukuphakamisa iziko |
Uluhlu lolawulo lwe-Servo | 0.01mm-0.5mm/Min |
Isantya sokubuya ngokukhawuleza se-crucible | 80-100mm/Umzuzu |